Leghe Austenitiche

LEGHE AUSTENITICHE
Designazione

ACI/ASTM DIN AFNOR UNS Altre
CF20 A743 CF20 1.4312 GX10CrNi188 Z10CN18.9M - -
CF8 A351 CF8 1.4308 GX6CrNi189 Z6CN18.10M J92600 AISI 304 (5)
CF8A A351 CF8A - - J92600 AISI 304H (5)
CF8C A351 CF8C 1.4552 GX5CrNiNb189 Z6CNNb18.10M J92910 AISI 347 (5)
CF3 A351 CF3 1.4306 X2CrNi1911 (5) Z2CN18.10M J92500 AISI 304L (5)
CF3A A351 CF3A - - J92500 -
CF8M A351 CF8M 1.4408 GX6CrNiMo1810 Z6CND18.12M J92900 AISI 316 (5)
CF8MNb A351 CF10MC 1.4851 GX5CrNiMoNb1810 Z6CNDNb18.12M - AISI 316Nb (5)
CF3M A351 CF3M 1.4404 X2CrNiMo17122 (5) Z2CND18.12M J92800 AISI 316L (5)
CF3MS AISI316LS (5) 1.4435 X2CrNiMo18143 (5) - - AISI 316LS (5)
CF3MN A351 CF3MN - - - AISI 316LN (5)
CF16F A743 CF16F - - J92701 AISI 303 (5)
CG8M A351 CG8M - - J93000 AISI 317 (5)
1.4439 - 1.4439 GX3CrNiMoN17135 - - -
CK20 A351 CK20 - - J94202 AISI 310S (5)
316HP - - - - (6)
316LHP - - - - (6)
Composizione chimica

C Cr Ni Mo Altri Trattamento termico (1) Microstruttura (2)
CF20 < 0.20 19.5 9.5 - - S a
CF8 < 0.08 19.5 9.5 < 0.5 - S a, (f)
CF8A < 0.08 19.5 9.5 < 0.5 - S a, (f)
CF8C < 0.08 19.5 10.5 < 0.5 Nb>8x%C S a, (f)
CF3 < 0.03 19.0 10.0 < 0.5 - S a, (f)
CF3A < 0.03 19.0 10.0 < 0.5 - S a, (f)
CF8M < 0.08 19.5 10.5 2.3 - S a, (f)
CF8MNb < 0.08 19.5 10.5 2.3 Nb>8x%C S a, (f)
CF3M < 0.03 19.0 11.0 2.3 - S a, (f)
CF3MS < 0.03 19.0 13.5 2.7 - S a
CF3MN < 0.03 19.0 11.0 2.3 0.15N S a
CF16F < 0.16 19.5 10.5 < 1.5 S, (P), (Se) S a, (f, i)
CG8M < 0.08 19.5 11.0 3.5 - S a
1.4439 < 0.03 17.5 13.5 4.5 0.17N S a
CK20 < 0.20 25.0 20.5 < 0.5 - S a
316HP < 0.07 21.0 9.0 2.3 0.12N S a, (f)
316LHP < 0.03 21.0 9.0 2.3 0.12N S a, (f)
Proprietà meccaniche e fisiche

Limite elastico 0.2% MPa min Rottura MPa min Allungamento %min Durezza HB (3) Resilienza KV J (3) Densità Kg/dm3 Ritiro lineare Saldabilità (4)
CF20 205 485 30 150-200 80 7.75 2.7% 1
CF8 205 485 35 140-200 120 7.75 2.6% 1
CF8A 240 530 35 150-200 110 7.75 2.6% 1
CF8C 205 485 30 140-200 80 7.75 2.7% 1
CF3 205 485 35 140-200 140 7.75 2.6% 1
CF3A 240 530 35 150-200 120 7.75 2.6% 1
CF8M 205 485 30 140-200 120 7.75 2.6% 1
CF8MNb 205 485 25 140-200 110 7.75 2.7% 2
CF3M 205 485 30 140-200 120 7.75 2.6% 1
CF3MS 205 485 25 140-200 120 7.75 2.6% 1
CF3MN 255 515 35 150-200 140 7.75 2.6% 1
CF16F 205 485 30 140-200 100 7.75 2.6% 2
CG8M 240 515 25 150-200 100 7.75 2.6% 1
1.4439 210 490 20 140-200 120 7.75 2.6% 1
CK20 195 450 30 150-220 80 7.75 2.7% 2
316HP 300 550 35 150-200 120 7.75 2.6% 1
316LHP 300 550 35 150-200 120 7.75 2.6% 1
(1) A: Ricotto; N: Normalizzato e rinvenuto; H: Bonificato; S: Solubilizzato; P: Invecchiato per precipitazione; () Opzionale.
(2) a: Austenite; f: Ferrite delta; m: Martensite; i: Fasi intermetalliche; (): Fase secondaria.
(3) Valori tipici a 20° C.
(4) 1: Molto buona; 2: Buona; 3: Discreta con precauzioni; 4: Generalmente scarsa.
(5) Corrispondente laminato